rate my first selfmade PCB ever.

>>55241025
Neat/10

>>55241025
Which method?
Looks like you didn't clean the PCB well enough before applying the design which caused it to etch poorly or your etching solution wasn't strong enough.

As far as PCB design goes, generally you'd want to avoid having 90 degree edges on your traces.

Other than that, good work!

>>55241056
>Which method?
with direct toner method.
I needed a few tries to apply the toner properly. Could be possible that there have been residues from the multiple "cleaning"
>>55241056
>As far as PCB design goes, generally you'd want to avoid having 90 degree edges on your traces.
why is that? Ill keep it in mind though. thanks.

>>55241056
>>55241086
PS: I used iron III chlorid. Not even sure if that's the correct term in english.

File: IMG_20150128_113727.jpg (1MB, 2560x1920px) Image search: [Google]

1MB, 2560x1920px

r8

>>55241086
Well, apparently 90 degree angles cause more EMI at higher frequency circuits, but there's a lot of conflicting information about that.

>>55241109
Ah, Ferric Chloride.
I use Copper Chloride since you can re-use it after etching.

>>55241143
>>55241158
naise.
would use/10

>>55241025
Should have been named "Transgressor". Otherwise it is excellent.

File: 1466797438875.jpg (870KB, 2736x1632px) Image search: [Google]

870KB, 2736x1632px

>>55241025
I give it a meme/10

File: 2jHUk8i.png (117KB, 1444x1258px) Image search: [Google]

117KB, 1444x1258px

>>55241222
nice trips and awesome meme :^)

>>55241176
>>55241109
Wait is this something you can do at home? I always assumed you needed to send out to some Chinese shop to get a custom board.

>>55241158
Nice click ahmed

>>55241247
sure.
Depends on the method you are using though.

>>55241247
It was a uni project I did in 4th semester. Used the uni lab but did literally everything myself.

>>55241265
Allahu ackbar.

>>55241025
>90 degree traces
Cmon op...

>>55241374
I didn't even know about that. Blease be nice :(
I'll rework the layout.

>>55241169
with traces that wide, there shouldnt be any issue

with 1-2mm traces thats a mild issue, smaller and its noticable

>>55241247
Yes, but you can only do two-sided boards and you can't do very small traces/pads because the dissolving of the copper is not very uniform.

You also won't get a solder mask or plating on the insides of the holes, so soldering is not as easy as on a "real" board.

Neat

>>55241025
Can you post the schematic m8?

File: 1466186719696.jpg (137KB, 1000x1000px) Image search: [Google]

137KB, 1000x1000px

good shit keep at it we will need you soon.

This looks neat as fuck. How would one go about making their own? Anyone have any pointers?

>>55241540
No, I am in bed now.
>>55241645
download eagle
design schematic
read tutorial
????
profit

>>55241730
Thanks, appreciate it.

Sweet dreams OP

Good job OP
You posted actual technology on this board

>>55241025
>traces at 90° angles
m8 its like you want the electrons to fly off and kill an innocent bystander

OP is not a faggot and is a true /g/ man.

props.